EN GJS 700-2 hardened & tempered, nodular graphite, Mechanical Properties | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY

EN GJS 700-2 hardened & tempered, nodular graphite, Mechanical Properties
Young’s modulus 168 – 176 GPa
Flexural modulus * 168 – 176 GPa
Shear modulus 65 – 70 GPa
Bulk modulus 121 – 134 GPa
Poisson’s ratio 0.27 – 0.28
Shape factor 19
Yield strength (elastic limit) 550 – 630 MPa
Tensile strength 700 – 800 MPa
Compressive strength * 559 – 639 MPa
Flexural strength (modulus of rupture) 550 – 630 MPa
Elongation 2 – 7 % strain
Hardness – Vickers 235 – 265 HV
Fatigue strength at 10^7 cycles 280 – 304 MPa
Fatigue strength model (stress range) 188 – 234 MPa
Parameters: Stress Ratio = 0, Number of Cycles = 1e7
Fracture toughness 22 – 34 MPa.m^0.5
Mechanical loss coefficient (tan delta) * 6e-4 – 0.001
*Values are approximations. This information’s accuracy is not guaranteed.
Sand Casting Investment Casting Foundry Pouring Gray Ductile Nodular Products Parts Manufacturing Machining CNC Supplier in Turkey
Cast iron, nodular graphite, EN GJS 700-2, hardened & tempered Equivalent Grades | Modulus Metal | Supplier | Foundry | Castings Products | in TURKEY
EN GJS 700 2, hardened & tempered, Chemical Composition (Cast iron, nodular graphite) | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY
Posted on

EN GJS 700-2 as cast & normalized, nodular graphite, Mechanical Properties | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY

EN GJS 700-2 as cast & normalized, nodular graphite, Mechanical Properties
Young’s modulus 172 – 180 GPa
Flexural modulus * 172 – 180 GPa
Shear modulus 67 – 71 GPa
Bulk modulus 124 – 137 GPa
Poisson’s ratio 0.27 – 0.28
Shape factor 21
Yield strength (elastic limit) 416 – 471 MPa
Tensile strength 700 – 800 MPa
Compressive strength * 425 – 480 MPa
Flexural strength (modulus of rupture) 416 – 471 MPa
Elongation 2 – 5 % strain
Hardness – Vickers 250 – 270 HV
Fatigue strength at 10^7 cycles 280 – 304 MPa
Fatigue strength model (stress range) 188 – 234 MPa
Parameters: Stress Ratio = 0, Number of Cycles = 1e7
Fracture toughness 22 – 34 MPa.m^0.5
Mechanical loss coefficient (tan delta) * 8e-4 – 0.0012
*Values are approximations. This information’s accuracy is not guaranteed.
Sand Casting Investment Casting Foundry Pouring Gray Ductile Nodular Products Parts Manufacturing Machining CNC Supplier in Turkey Turquie
EN GJS 700-2, as cast & normalized, Chemical Composition (Cast iron, nodular graphite) | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY
Cast iron, nodular graphite, EN GJS 700-2, as cast & normalized Equivalent Grades | Modulus Metal | Supplier | Foundry | Castings Products | in TURKEY
Posted on

EN GJS 600 3 Cast iron, nodular graphite, Mechanical Properties | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY

EN GJS 600 3 Cast iron, nodular graphite, Mechanical Properties
Young’s modulus 170 – 180 GPa
Flexural modulus * 170 – 180 GPa
Shear modulus 66 – 71 GPa
Bulk modulus 123 – 137 GPa
Poisson’s ratio 0.27 – 0.28
Shape factor 22
Yield strength (elastic limit) 370 – 415 MPa
Tensile strength 600 – 700 MPa
Compressive strength * 382 – 425 MPa
Flexural strength (modulus of rupture) 372 – 416 MPa
Elongation 3 – 7 % strain
Hardness – Vickers 220 – 255 HV
Fatigue strength at 10^7 cycles 248 – 280 MPa
Fatigue strength model (stress range) 165 – 212 MPa
Parameters: Stress Ratio = 0, Number of Cycles = 1e7
Fracture toughness * 22 – 54 MPa.m^0.5
Mechanical loss coefficient (tan delta) * 0.001 – 0.0012
*Values are approximations. This information’s accuracy is not guaranteed.
Sand Casting Investment Casting Foundry Pouring Gray Ductile Nodular Products Parts Manufacturing Machining CNC Supplier in Turkey Turkei Turquie
EN GJS 600 3 Chemical Composition (Cast iron, nodular graphite) | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY
Cast iron, nodular graphite, EN GJS 600 3 Equivalent Grades | Modulus Metal | Supplier | Foundry | Castings Products | in TURKEY
Posted on

EN GJS 500 7 Cast iron, nodular graphite, Mechanical Properties | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY

EN GJS 500 7 Cast iron, nodular graphite, Mechanical Properties
Young’s modulus 165 – 178 GPa
Flexural modulus * 165 – 178 GPa
Shear modulus 64 – 71 GPa
Bulk modulus 119 – 135 GPa
Poisson’s ratio 0.27 – 0.28
Shape factor 23
Yield strength (elastic limit) 320 – 370 MPa
Tensile strength 500 – 600 MPa
Compressive strength * 351 – 382 MPa
Flexural strength (modulus of rupture) 339 – 372 MPa
Elongation 7 – 15 % strain
Hardness – Vickers 175 – 225 HV
Fatigue strength at 10^7 cycles 224 – 248 MPa
Fatigue strength model (stress range) 142 – 190 MPa
Parameters: Stress Ratio = 0, Number of Cycles = 1e7
Fracture toughness * 22 – 54 MPa.m^0.5
Mechanical loss coefficient (tan delta) * 0.001 – 0.0014
*Values are approximations. This information’s accuracy is not guaranteed.
Sand Casting Investment Casting Foundry Gray Ductile Nodular Steel Products Parts Manufacturing Machining CNC Supplier in Turkey
EN GJS 500 7 Chemical Composition (Cast iron, nodular graphite) | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY
Cast iron, nodular graphite, EN GJS 500 7 Equivalent Grades | Modulus Metal | Supplier | Foundry | Castings Products | in TURKEY
Posted on

EN GJS 450 10 Cast iron, nodular graphite, Mechanical Properties | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY

EN GJS 450 10 Cast iron, nodular graphite, Mechanical Properties
Young’s modulus 165 – 173 GPa
Flexural modulus * 165 – 173 GPa
Shear modulus 64 – 69 GPa
Bulk modulus 119 – 132 GPa
Poisson’s ratio 0.27 – 0.28
Shape factor 23
Yield strength (elastic limit) 305 – 339 MPa
Tensile strength 450 – 500 MPa
Compressive strength * 319 – 351 MPa
Flexural strength (modulus of rupture) 305 – 339 MPa
Elongation 10 – 18 % strain
Hardness – Vickers 160 – 180 HV
Fatigue strength at 10^7 cycles 210 – 224 MPa
Fatigue strength model (stress range) 136 – 162 MPa
Parameters: Stress Ratio = 0, Number of Cycles = 1e7
Fracture toughness * 22 – 54 MPa.m^0.5
Mechanical loss coefficient (tan delta) * 0.0012 – 0.0016
*Values are approximations. This information’s accuracy is not guaranteed.
Sand Casting Investment Casting Foundry Gray Ductile Nodular Products Parts Manufacturing Machining CNC Supplier in Turkey Turkei
EN GJS 450 10 Chemical Composition (Cast iron, nodular graphite) | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY
Cast iron, nodular graphite, EN GJS 450 10 Equivalent Grades | Modulus Metal | Supplier | Foundry | Castings Products | in TURKEY
Posted on

EN GJS 400 18 U Cast iron, nodular graphite, Mechanical Properties | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY

EN GJS 400 18 U Cast iron, nodular graphite, Mechanical Properties
Young’s modulus 165 – 173 GPa
Flexural modulus * 165 – 173 GPa
Shear modulus 64 – 69 GPa
Bulk modulus 119 – 132 GPa
Poisson’s ratio 0.27 – 0.28
Shape factor 24
Yield strength (elastic limit) 232 – 259 MPa
Tensile strength 370 – 400 MPa
Compressive strength * 246 – 273 MPa
Flexural strength (modulus of rupture) 232 – 259 MPa
Elongation * 17 – 28 % strain
Hardness – Vickers 124 – 140 HV
Fatigue strength at 10^7 cycles 186 – 195 MPa
Fatigue strength model (stress range) * 118 – 137 MPa
Parameters: Stress Ratio = 0, Number of Cycles = 1e7
Fracture toughness 33 – 54 MPa.m^0.5
Mechanical loss coefficient (tan delta) * 0.0016 – 0.002
*Values are approximations. This information’s accuracy is not guaranteed.
Sand Casting Investment Casting Foundry Gray Ductile Nodular Products Parts Manufacturing Machining CNC Supplier in Turkey Turkei
Cast iron, nodular graphite, EN GJS 400 18U Equivalent Grades | Modulus Metal | Supplier | Foundry | Castings Products | in TURKEY
EN GJS 400 18U Chemical Composition (Cast iron, nodular graphite) | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY
Posted on

EN GJS 400 18 LT Cast iron, nodular graphite, Mechanical Properties | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY

EN GJS 400 18 LT Cast iron, nodular graphite, Mechanical Properties
Young’s modulus 165 – 173 GPa
Flexural modulus * 165 – 173 GPa
Shear modulus 64 – 69 GPa
Bulk modulus 119 – 132 GPa
Poisson’s ratio 0.27 – 0.28
Shape factor 24
Yield strength (elastic limit) 240 – 280 MPa
Tensile strength 400 – 420 MPa
Compressive strength * 273 – 292 MPa
Flexural strength (modulus of rupture) 259 – 278 MPa
Elongation 18 – 27 % strain
Hardness – Vickers 135 – 150 HV
Fatigue strength at 10^7 cycles 195 – 201 MPa
Fatigue strength model (stress range) 127 – 140 MPa
Parameters: Stress Ratio = 0, Number of Cycles = 1e7
Fracture toughness 33 – 54 MPa.m^0.5
Mechanical loss coefficient (tan delta) * 0.0016 – 0.0018
*Values are approximations. This information’s accuracy is not guaranteed.
Quick Test Cap Anlaysis Sand Casting Investment Casting Foundry Pouring Gray Ductile Nodular Products Parts Manufacturing Machining CNC Supplier in Turkey Turquie
Cast iron, nodular graphite, EN GJS 400 18 LT Equivalent Grades | Modulus Metal | Supplier | Foundry | Castings Products | in TURKEY
EN GJS 400 18 LT Chemical Composition (Cast iron, nodular graphite) | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY
Posted on

EN GJS 400 18 Cast iron, nodular graphite, Mechanical Properties | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY

EN GJS 400 18 Cast iron, nodular graphite, Mechanical Properties
Young’s modulus 165 – 173 GPa
Flexural modulus * 165 – 173 GPa
Shear modulus 64 – 69 GPa
Bulk modulus 119 – 132 GPa
Poisson’s ratio 0.27 – 0.28
Shape factor 24
Yield strength (elastic limit) 250 – 280 MPa
Tensile strength 400 – 420 MPa
Compressive strength * 273 – 292 MPa
Flexural strength (modulus of rupture) 259 – 278 MPa
Elongation 18 – 27 % strain
Hardness – Vickers 135 – 150 HV
Fatigue strength at 10^7 cycles 195 – 201 MPa
Fatigue strength model (stress range) 127 – 140 MPa
Parameters: Stress Ratio = 0, Number of Cycles = 1e7
Fracture toughness 33 – 54 MPa.m^0.5
Mechanical loss coefficient (tan delta) * 0.0016 – 0.0018
*Values are approximations. This information’s accuracy is not guaranteed.
Sand Casting Molding Moulage Sandguss Au Sable Modulus Metal Turkiye Turkey Turkei Turquie
Cast iron, nodular graphite, EN GJS 400 18 Equivalent Grades | Modulus Metal | Supplier | Foundry | Castings Products | in TURKEY
EN GJS 400 18 Chemical Composition (Cast iron, nodular graphite) | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY
Posted on

EN GJS 400 15U <30mm Cast iron, nodular graphite, Mechanical Properties | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY

EN GJS 400 15U <30mm Cast iron, nodular graphite, Mechanical Properties
Young’s modulus 165 – 173 GPa
Flexural modulus * 165 – 173 GPa
Shear modulus 64 – 69 GPa
Bulk modulus 119 – 132 GPa
Poisson’s ratio 0.27 – 0.28
Shape factor 24
Yield strength (elastic limit) 250 – 305 MPa
Tensile strength 400 – 450 MPa
Compressive strength * 292 – 319 MPa
Flexural strength (modulus of rupture) 278 – 305 MPa
Elongation 12 – 20 % strain
Hardness – Vickers 145 – 165 HV
Fatigue strength at 10^7 cycles 201 – 210 MPa
Fatigue strength model (stress range) 126 – 152 MPa
Parameters: Stress Ratio = 0, Number of Cycles = 1e7
Fracture toughness 33 – 54 MPa.m^0.5
Mechanical loss coefficient (tan delta) * 0.0014 – 0.0018
*Values are approximations. This information’s accuracy is not guaranteed.
Furnace Modulus Metal Sand Casting Investment Casting Foundry Pouring Gray Ductile Nodular Products Parts Manufacturing Machining CNC Supplier in Turkey Turquie
EN GJS 400 15U <30mm Chemical Composition (Cast iron, nodular graphite) | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY
Cast iron, nodular graphite, EN GJS 400 15U <30mm Equivalent Grades | Modulus Metal | Supplier | Foundry | Castings Products | in TURKEY
Posted on

EN GJS 350 22 LT Cast iron, nodular graphite, Mechanical Properties | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY

EN GJS 350 22 LT Cast iron, nodular graphite, Mechanical Properties
Young’s modulus 165 – 173 GPa
Flexural modulus * 165 – 173 GPa
Shear modulus 64 – 69 GPa
Bulk modulus 119 – 132 GPa
Poisson’s ratio 0.27 – 0.28
Shape factor 24
Yield strength (elastic limit) 215 – 259 MPa
Tensile strength 350 – 400 MPa
Compressive strength * 229 – 273 MPa
Flexural strength (modulus of rupture) 215 – 259 MPa
Elongation 22 – 29 % strain
Hardness – Vickers 115 – 140 HV
Fatigue strength at 10^7 cycles 180 – 195 MPa
Fatigue strength model (stress range) 112 – 138 MPa
Parameters: Stress Ratio = 0, Number of Cycles = 1e7
Fracture toughness 33 – 54 MPa.m^0.5
Mechanical loss coefficient (tan delta) * 0.0016 – 0.0022
*Values are approximations. This information’s accuracy is not guaranteed.
Modulus Metal olten-cast-iron Sand Casting Investment Casting Foundry Pouring Gray Ductile Nodular Products Parts Manufacturing Machining CNC Supplier in Turkey Turquie
EN GJS 350 22 LT Chemical Composition (Cast iron, nodular graphite) | Modulus Metal | Supplier | Foundry | Sand Casting | Investment Casting | Machining | Products | in TURKEY
Cast iron, nodular graphite, EN GJS 350 22 LT Equivalent Grades | Modulus Metal | Supplier | Foundry | Castings Products | in TURKEY