EN GJS 700-2 hardened & tempered, nodular graphite, Mechanical Properties
Young’s modulus 168 – 176 GPa
Flexural modulus * 168 – 176 GPa
Shear modulus 65 – 70 GPa
Bulk modulus 121 – 134 GPa
Poisson’s ratio 0.27 – 0.28
Shape factor 19
Yield strength (elastic limit) 550 – 630 MPa
Tensile strength 700 – 800 MPa
Compressive strength * 559 – 639 MPa
Flexural strength (modulus of rupture) 550 – 630 MPa
Elongation 2 – 7 % strain
Hardness – Vickers 235 – 265 HV
Fatigue strength at 10^7 cycles 280 – 304 MPa
Fatigue strength model (stress range) 188 – 234 MPa
Parameters: Stress Ratio = 0, Number of Cycles = 1e7
Fracture toughness 22 – 34 MPa.m^0.5
Mechanical loss coefficient (tan delta) * 6e-4 – 0.001
*Values are approximations. This information’s accuracy is not guaranteed.