Aluminum 6060 T6 Mechanical Properties

Designation
6060, wrought
Condition	T6 (Solution heat-treated and artificially aged)
UNS number	A96060
EN name	EN AW-6060 (EN AW-Al MgSi)
EN number	3.3206

Aluminum 6060 T6 Mechanical Properties

Young’s modulus	69.5	–	73	GPa
Specific stiffness	25.6	–	26.9	MN.m/kg
Yield strength (elastic limit)	150	–	175	MPa
Tensile strength	190	–	222	MPa
Specific strength	55.3	–	64.5	kN.m/kg
Elongation	8	–	11.5	% strain
Compressive modulus	69.3	–	72.8	GPa
Compressive strength	150	–	175	MPa
Flexural modulus	69.5	–	73	GPa
Flexural strength (modulus of rupture)	150	–	175	MPa
Shear modulus	25	–	27	GPa
Shear strength	139	–	162	MPa
Bulk modulus	69.5	–	73	GPa
Poisson’s ratio	0.325	–	0.335
Shape factor	34.5
Hardness – Vickers	86	–	95	HV
Hardness – Brinell	81	–	89.2	HB
Elastic stored energy (springs)	159	–	214	kJ/m^3
Fatigue strength at 10^7 cycles	68.4	–	79.8	MPa
Fatigue strength model (stress range) Parameters: Stress Ratio = -1, Number of Cycles = 1e7cycles	62.5	–	87.3	MPa