Aluminum 6005A T6 Mechanical Properties

Designation: Aluminum 6005A T6

6005A, wrought
Condition	T6 (Solution heat-treated and artificially aged)
UNS number	A96005A
EN name	EN AW-6005A
EN number	3.3210
ISO name	Al SiMg(A)
JIS (Japanese) name	A6NO1

Mechanical properties: Aluminum 6005A T6

Young’s modulus	67.8	–	71.2	GPa
Specific stiffness	25	–	26.3	MN.m/kg
Yield strength (elastic limit)	225	–	262	MPa
Tensile strength	270	–	315	MPa
Specific strength	83	–	96.8	kN.m/kg
Elongation	8	–	11.5	% strain
Compressive strength	225	–	262	MPa
Flexural modulus	67.8	–	71.2	GPa
Flexural strength (modulus of rupture)	225	–	262	MPa
Shear modulus	27.1	–	28.5	GPa
Shear strength	162	–	189	MPa
Bulk modulus	67.8	–	71.2	GPa
Poisson’s ratio	0.325	–	0.335
Shape factor	26.4
Hardness – Vickers	90	–	100	HV
Hardness – Brinell	85	–	95.3	HB
Elastic stored energy (springs)	366	–	492	kJ/m^3
Fatigue strength at 10^7 cycles	97.4	–	114	MPa
Fatigue strength model (stress range) Parameters: Stress Ratio = -1, Number of Cycles = 1e7cycles	89.2	–	124	MPa