Aluminum 6082 T4 Mechanical Properties

Designation
6082, wrought
Condition	T4 (Solution heat-treated and naturally aged to a substantially stable condition)
UNS number	A96082
EN name	EN AW-6082 (EN AW-Al Si1MgMn)
EN number	3.2315

Aluminum 6082 T4 Mechanical Properties

Young’s modulus	70	–	74	GPa
Specific stiffness	25.9	–	27.5	MN.m/kg
Yield strength (elastic limit)	115	–	134	MPa
Tensile strength	190	–	222	MPa
Specific strength	42.6	–	49.7	kN.m/kg
Elongation	15	–	21.6	% strain
Compressive strength	115	–	134	MPa
Flexural modulus	70	–	74	GPa
Flexural strength (modulus of rupture)	115	–	134	MPa
Shear modulus	25.3	–	26.6	GPa
Shear strength	157	–	184	MPa
Bulk modulus	70	–	74	GPa
Poisson’s ratio	0.325	–	0.335
Shape factor	38.2
Hardness – Vickers	71	–	79	HV
Hardness – Brinell	67	–	74	HB
Elastic stored energy (springs)	92.2	–	124	kJ/m^3
Fatigue strength at 10^7 cycles	82.7	–	96.4	MPa
Fatigue strength model (stress range) Parameters: Stress Ratio = -1, Number of Cycles = 1e7cycles	75.4	–	106	MPa