Aluminum 6060 T4 Mechanical Properties

Designation
6060, wrought
Condition	T4 (Solution heat-treated and naturally aged to a substantially stable condition)
UNS number	A96060
EN name	EN AW-6060 (EN AW-Al MgSi)
EN number	3.3206

Aluminum 6060 T4 Mechanical Properties

Young’s modulus	69.5	–	73	GPa
Specific stiffness	25.7	–	27.1	MN.m/kg
Yield strength (elastic limit)	60	–	70	MPa
Tensile strength	130	–	152	MPa
Specific strength	22.2	–	25.9	kN.m/kg
Elongation	15	–	21.6	% strain
Compressive strength	60	–	70	MPa
Flexural modulus	69.5	–	73	GPa
Flexural strength (modulus of rupture)	60	–	70	MPa
Shear modulus	25	–	27	GPa
Shear strength	97.2	–	113	MPa
Bulk modulus	69.5	–	73	GPa
Poisson’s ratio	0.325	–	0.335
Shape factor	41.6
Hardness – Vickers	52	–	58	HV
Hardness – Brinell	48	–	53	HB
Elastic stored energy (springs)	25.4	–	34.3	kJ/m^3
Fatigue strength at 10^7 cycles	56.4	–	65.8	MPa
Fatigue strength model (stress range) Parameters: Stress Ratio = -1, Number of Cycles = 1e7cycles	51.4	–	72.2	MPa