Category: Stainless_Steels

Posted on

UNS S32760 vs LDX 2101 ( 1.4501 vs 1.4162 )

UNS S32760 vs LDX 2101 ( 1.4501 vs 1.4162 )

PropertyUNS S32760 (1.4501 / F55 · Zeron 100)LDX 2101 (1.4162 / S32101)
COMPOSITION (%)
Cr (chromium)24 – 2621 – 22
Ni (nickel)6 – 81.35 – 1.7
Mo (molybdenum)3 – 40.1 – 0.8
N (nitrogen)0.2 – 0.30.2 – 0.25
Cu (copper)0.5 – 10.1 – 0.8
Mn (manganese)0 – 14 – 6
W (tungsten)0.5 – 1—
PHYSICAL
Density (g/cm3)7.73 – 7.827.69 – 7.76
MECHANICAL
Young’s Modulus (GPa)190 – 200195 – 205
Yield Strength (MPa)515 – 565480 – 600
Tensile Strength (MPa)700 – 930700 – 840
Elongation (% strain)23 – 2735 – 38
Hardness – Brinell (HB)276 – 286222 – 233
Hardness – Rockwell C2821 – 22
Fatigue Strength @ 10^7 (MPa)241 – 267470 – 530
Fracture Toughness (MPa*m^0.5)150 – 195144 – 176
THERMAL
Melting Point (C)1400 – 14501400 – 1450
Max Service Temp (C)335 – 365335 – 365
Min Service Temp (C)-60 – -50-60 – -50
Thermal Conductivity (W/m*C)12.9 – 1514.4 – 15.6
CORROSION RESISTANCE
PREN37.9 – 45.724.5 – 28.6
Pitting & Crevice CorrosionVery High (>40)Medium (20-30)
Stress Corrosion CrackingSlightly SusceptibleSlightly Susceptible
Sea WaterExcellentGood
Sour Oil & GasGoodGood
PROCESSING
Machining Speed (m/min)14.623.8
WeldabilityGood (MIG/plasma/SAW/TIG: Excellent)Good (MIG/plasma/SAW/TIG: Good)
Metal CastingUnsuitableUnsuitable
Metal Hot FormingLimited useAcceptable
Carbon Equivalency1.12 – 1.40.866 – 1.12
NOTES
Generation / Notes2nd generation duplex—
Typical Uses——
Overview · All Grades
Duplex & Semi-Austenitic Stainless Steels
Material Group Page
Cast Grades
Water Quenched · Cast
ASTM CD-4MCu
Material Data Sheet
Wrought Grades
Wrought · Duplex
UNS S32003 / AL 2003
Material Data Sheet
Wrought · Duplex
LDX 2101
Material Data Sheet
Wrought · Duplex
AISI 329
Material Data Sheet
Wrought · Duplex
AISI 2205
Material Data Sheet
Wrought · Duplex
UNS S32550
Material Data Sheet
Wrought · Duplex
UNS S32760
Material Data Sheet
Posted on

UNS S32760 vs AISI 329

UNS S32760 vs AISI 329

PropertyUNS S32760 (1.4501 / F55 · Zeron 100)AISI 329 (S32900 · 1st generation)
COMPOSITION (%)
Cr (chromium)24 – 2623 – 28
Ni (nickel)6 – 82 – 5
Mo (molybdenum)3 – 41 – 2
N (nitrogen)0.2 – 0.3—
Cu (copper)0.5 – 1—
Mn (manganese)0 – 10 – 1
W (tungsten)0.5 – 1—
PHYSICAL
Density (g/cm3)7.73 – 7.827.7 – 7.9
MECHANICAL
Young’s Modulus (GPa)190 – 200189 – 204
Yield Strength (MPa)515 – 565500 – 600
Tensile Strength (MPa)700 – 930650 – 795
Elongation (% strain)23 – 2720 – 35
Hardness – Brinell (HB)276 – 286130 – 150
Hardness – Rockwell C280 – 4
Fatigue Strength @ 10^7 (MPa)241 – 267316 – 365
Fracture Toughness (MPa*m^0.5)150 – 19571 – 110
THERMAL
Melting Point (C)1400 – 14501380 – 1450
Max Service Temp (C)335 – 365740 – 787
Min Service Temp (C)-60 – -50-150
Thermal Conductivity (W/m*C)12.9 – 1515 – 21
CORROSION RESISTANCE
PREN37.9 – 45.726.3 – 34.6
Pitting & Crevice CorrosionVery High (>40)High (30-40)
Stress Corrosion CrackingSlightly SusceptibleSusceptible
Sea WaterExcellentModerate
Sour Oil & GasGoodModerate
PROCESSING
Machining Speed (m/min)14.625.6
WeldabilityGood (MIG/plasma/SAW/TIG: Excellent)Good (MIG/plasma/SAW/TIG: Good)
Metal CastingUnsuitableUnsuitable
Metal Hot FormingLimited useAcceptable
Carbon Equivalency1.12 – 1.40.867 – 1.29
NOTES
Generation / Notes2nd generation duplex1st generation duplex, no longer produced much
Typical Uses—Processing of potentially corrosive liquids (chemicals/oil/beverages/sewage); structural uses in corrosive environments e.g. nuclear plants, ships, offshore oil installations, underwater cables and pipes
Overview · All Grades
Duplex & Semi-Austenitic Stainless Steels
Material Group Page
Cast Grades
Water Quenched · Cast
ASTM CD-4MCu
Material Data Sheet
Wrought Grades
Wrought · Duplex
UNS S32003 / AL 2003
Material Data Sheet
Wrought · Duplex
LDX 2101
Material Data Sheet
Wrought · Duplex
AISI 329
Material Data Sheet
Wrought · Duplex
AISI 2205
Material Data Sheet
Wrought · Duplex
UNS S32550
Material Data Sheet
Wrought · Duplex
UNS S32760
Material Data Sheet
Posted on

UNS S32760 vs AISI 2205 (1.4501 vs 1.4462)

UNS S32760 vs AISI 2205 (1.4501 vs 1.4462)

PropertyUNS S32760 (1.4501 / F55 · Zeron 100)AISI 2205 (1.4462 / S31803–S32205)
COMPOSITION (%)
Cr (chromium)24 – 2621 – 23
Ni (nickel)6 – 84.5 – 6.5
Mo (molybdenum)3 – 42.5 – 3.5
N (nitrogen)0.2 – 0.30.08 – 0.2
Cu (copper)0.5 – 1—
Mn (manganese)0 – 10 – 2
W (tungsten)0.5 – 1—
PHYSICAL
Density (g/cm3)7.73 – 7.827.8 – 7.82
MECHANICAL
Young’s Modulus (GPa)190 – 200195 – 205
Yield Strength (MPa)515 – 565460 – 510
Tensile Strength (MPa)700 – 930640 – 950
Elongation (% strain)23 – 2720 – 25
Hardness – Brinell (HB)276 – 286278 – 308
Hardness – Rockwell C2822 – 31
Fatigue Strength @ 10^7 (MPa)241 – 267261 – 289
Fracture Toughness (MPa*m^0.5)150 – 195144 – 195
THERMAL
Melting Point (C)1400 – 14501400 – 1450
Max Service Temp (C)335 – 365335 – 365
Min Service Temp (C)-60 – -50-60 – -50
Thermal Conductivity (W/m*C)12.9 – 1514.4 – 15.6
CORROSION RESISTANCE
PREN37.9 – 45.730.5 – 37.8
Pitting & Crevice CorrosionVery High (>40)High (30-40)
Stress Corrosion CrackingSlightly SusceptibleNot Susceptible
Sea WaterExcellentGood
Sour Oil & GasGoodGood
PROCESSING
Machining Speed (m/min)14.615.8
WeldabilityGood (MIG/plasma/SAW/TIG: Excellent)Good (MIG/plasma/SAW/TIG: Good)
Metal CastingUnsuitableUnsuitable
Metal Hot FormingLimited useAcceptable
Carbon Equivalency1.12 – 1.40.942 – 1.24
NOTES
Generation / Notes2nd generation duplex2nd generation duplex
Typical Uses——
Overview · All Grades
Duplex & Semi-Austenitic Stainless Steels
Material Group Page
Cast Grades
Water Quenched · Cast
ASTM CD-4MCu
Material Data Sheet
Wrought Grades
Wrought · Duplex
UNS S32003 / AL 2003
Material Data Sheet
Wrought · Duplex
LDX 2101
Material Data Sheet
Wrought · Duplex
AISI 329
Material Data Sheet
Wrought · Duplex
AISI 2205
Material Data Sheet
Wrought · Duplex
UNS S32550
Material Data Sheet
Wrought · Duplex
UNS S32760
Material Data Sheet
Posted on

UNS S32760 vs ASTM CD-4MCu

UNS S32760 vs ASTM CD-4MCu

PropertyUNS S32760 (1.4501 / F55 · Zeron 100)ASTM CD-4MCu (J93370 · Cast)
COMPOSITION (%)
Cr (chromium)24 – 2624.5 – 26.5
Ni (nickel)6 – 84.75 – 6
Mo (molybdenum)3 – 41.75 – 2.25
N (nitrogen)0.2 – 0.3—
Cu (copper)0.5 – 12.75 – 3.25
Mn (manganese)0 – 10 – 1
W (tungsten)0.5 – 1—
PHYSICAL
Density (g/cm3)7.73 – 7.827.7 – 7.8
MECHANICAL
Young’s Modulus (GPa)190 – 200195 – 205
Yield Strength (MPa)515 – 565505 – 620
Tensile Strength (MPa)700 – 930670 – 820
Elongation (% strain)23 – 2730 – 40
Hardness – Brinell (HB)276 – 286228 – 258
Hardness – Rockwell C2821 – 26
Fatigue Strength @ 10^7 (MPa)241 – 267323 – 373
Fracture Toughness (MPa*m^0.5)150 – 19551 – 112
THERMAL
Melting Point (C)1400 – 14501460 – 1500
Max Service Temp (C)335 – 365746 – 770
Min Service Temp (C)-60 – -50-23 – -3
Thermal Conductivity (W/m*C)12.9 – 1515 – 16
CORROSION RESISTANCE
PREN37.9 – 45.730.3 – 33.9
Pitting & Crevice CorrosionVery High (>40)High (30-40)
Stress Corrosion CrackingSlightly SusceptibleSusceptible
Sea WaterExcellent—
Sour Oil & GasGood—
PROCESSING
Machining Speed (m/min)14.617.4
WeldabilityGood (MIG/plasma/SAW/TIG: Excellent)Good
Metal CastingUnsuitableLimited use
Metal Hot FormingLimited useUnsuitable
Carbon Equivalency1.12 – 1.41.1 – 1.35
NOTES
Generation / Notes2nd generation duplexMust be used in solution annealed condition
Typical Uses—Chemicals industry, marine, water supply, power plant, pulp & paper manufacture, soap manufacture, textiles, transportation
Overview · All Grades
Duplex & Semi-Austenitic Stainless Steels
Material Group Page
Cast Grades
Water Quenched · Cast
ASTM CD-4MCu
Material Data Sheet
Wrought Grades
Wrought · Duplex
UNS S32003 / AL 2003
Material Data Sheet
Wrought · Duplex
LDX 2101
Material Data Sheet
Wrought · Duplex
AISI 329
Material Data Sheet
Wrought · Duplex
AISI 2205
Material Data Sheet
Wrought · Duplex
UNS S32550
Material Data Sheet
Wrought · Duplex
UNS S32760
Material Data Sheet
Posted on

UNS S32760 vs UNS S32550 ( 1.4501 vs 1.4507)

UNS S32760 vs UNS S32550 ( 1.4501 vs 1.4507)

PropertyUNS S32760 (1.4501 / F55 · Zeron 100)UNS S32550 (1.4507 / F61)
COMPOSITION (%)
Cr (chromium)24 – 2624 – 27
Ni (nickel)6 – 84.5 – 6.5
Mo (molybdenum)3 – 42.9 – 3.9
N (nitrogen)0.2 – 0.30.1 – 0.25
Cu (copper)0.5 – 11.5 – 2.5
Mn (manganese)0 – 10 – 1.5
W (tungsten)0.5 – 1—
PHYSICAL
Density (g/cm3)7.73 – 7.827.73 – 7.82
MECHANICAL
Young’s Modulus (GPa)190 – 200195 – 205
Yield Strength (MPa)515 – 565520 – 580
Tensile Strength (MPa)700 – 930730 – 810
Elongation (% strain)23 – 2723 – 27
Hardness – Brinell (HB)276 – 286240 – 264
Hardness – Rockwell C2828
Fatigue Strength @ 10^7 (MPa)241 – 267246 – 271
Fracture Toughness (MPa*m^0.5)150 – 195192 – 212
THERMAL
Melting Point (C)1400 – 14501400 – 1450
Max Service Temp (C)335 – 365335 – 365
Min Service Temp (C)-60 – -50-60 – -50
Thermal Conductivity (W/m*C)12.9 – 1513.3 – 17
CORROSION RESISTANCE
PREN37.9 – 45.735.2 – 43.9
Pitting & Crevice CorrosionVery High (>40)Very High (>40)
Stress Corrosion CrackingSlightly SusceptibleSusceptible
Sea WaterExcellentExcellent
Sour Oil & GasGoodGood
PROCESSING
Machining Speed (m/min)14.616.5
WeldabilityGood (MIG/plasma/SAW/TIG: Excellent)Good (MIG/plasma/SAW/TIG: Excellent)
Metal CastingUnsuitableUnsuitable
Metal Hot FormingLimited useAcceptable
Carbon Equivalency1.12 – 1.41.12 – 1.48
NOTES
Generation / Notes2nd generation duplex2nd generation duplex
Typical Uses——
Overview · All Grades
Duplex & Semi-Austenitic Stainless Steels
Material Group Page
Cast Grades
Water Quenched · Cast
ASTM CD-4MCu
Material Data Sheet
Wrought Grades
Wrought · Duplex
UNS S32003 / AL 2003
Material Data Sheet
Wrought · Duplex
LDX 2101
Material Data Sheet
Wrought · Duplex
AISI 329
Material Data Sheet
Wrought · Duplex
AISI 2205
Material Data Sheet
Wrought · Duplex
UNS S32550
Material Data Sheet
Wrought · Duplex
UNS S32760
Material Data Sheet
Posted on

AISI 204-Cu Stainless steel, Annealed, Austenitic | 1.4597 |  Toughness | Fracture Toughness

AISI 204-Cu Stainless steel-1.4597-X9CrMnCuNB17-8-3, S20430 Fracture Toughness Modulus Metal Turkey Turkiye

Modulus Metal | Manufacturer Company in TURKEY: Sand Casting | Investment Casting | Foundry | CNC Machining | Press Bending | Laser Cutting | Welding | Plastics Injection Molding |Turkiye

Fracture Toughness & ToughnessValues
Fracture toughness*133 – 147 MPa.m^0.5
Toughness (G)*89.9 – 110 kJ/m^2
*Values indicated with asterisks (*) are approximate. No guarantee is provided for the precision of this information.
		
AISI 204-Cu Stainless steel, Annealed, Austenitic | 1.4597 |  Carbon equivalency | Equivalent carbon content | CEV
AISI 204-Cu Stainless steel, Annealed, Austenitic | 1.4597 | Weldability  
AISI 204-Cu Stainless steel, Annealed, Austenitic | Mechanical Properties
AISI 204-Cu Stainless steel, Annealed, Austenitic | Chemical Composition  
AISI 204-Cu Stainless steel, Annealed, Austenitic | Designation | Equivalent Grades & Similar Grades  
Posted on

AISI 204-Cu Stainless steel, Annealed, Austenitic | 1.4597 |  Carbon equivalency | Equivalent carbon content | CEV

AISI 204-Cu Stainless steel-1.4597-X9CrMnCuNB17-8-3, S20430 Carbon equivalency Modulus Metal Turkey Turkiye

Modulus Metal | Manufacturer Company in TURKEY: Sand Casting | Investment Casting | Foundry | CNC Machining | Press Bending | Laser Cutting | Welding | Plastics Injection Molding |Turkiye

Carbon equivalency0.825 – 1.26
AISI 204-Cu Stainless steel, Annealed, Austenitic | 1.4597 |  Toughness | Fracture Toughness
AISI 204-Cu Stainless steel, Annealed, Austenitic | 1.4597 | Weldability  
AISI 204-Cu Stainless steel, Annealed, Austenitic | Mechanical Properties
AISI 204-Cu Stainless steel, Annealed, Austenitic | Chemical Composition  
AISI 204-Cu Stainless steel, Annealed, Austenitic | Designation | Equivalent Grades & Similar Grades  

Posted on

AISI 204-Cu Stainless steel, Annealed, Austenitic | 1.4597 | Weldability  

AISI 204-Cu Stainless steel-1.4597-X9CrMnCuNB17-8-3, S20430 Weldability Modulus Metal Turkey Turkiye Manufacturing

Modulus Metal | Manufacturer Company in TURKEY: Sand Casting | Investment Casting | Foundry | CNC Machining | Press Bending | Laser Cutting | Welding | Plastics Injection Molding |Turkiye

Weldability*Good
Weldability – MIGGood
Weldability – plasmaGood
Weldability – SAWGood
Weldability – TIGGood
BrazeabilityGood
*Notes: Preheating and post weld heat treatments may be required
AISI 204-Cu Stainless steel, Annealed, Austenitic | 1.4597 |  Toughness | Fracture Toughness
AISI 204-Cu Stainless steel, Annealed, Austenitic | 1.4597 |  Carbon equivalency | Equivalent carbon content | CEV
AISI 204-Cu Stainless steel, Annealed, Austenitic | Mechanical Properties
AISI 204-Cu Stainless steel, Annealed, Austenitic | Chemical Composition  
AISI 204-Cu Stainless steel, Annealed, Austenitic | Designation | Equivalent Grades & Similar Grades  
Posted on

AISI 204-Cu Stainless steel, Annealed, Austenitic | Mechanical Properties

AISI 204-Cu Stainless steel-1.4597-X9CrMnCuNB17-8-3, S20430 Mechanical Properties Modulus Metal Turkey Turkiye Manufacturing

Modulus Metal | Manufacturer Company in TURKEY: Sand Casting | Investment Casting | Foundry | CNC Machining | Press Bending | Laser Cutting | Welding | Plastics Injection Molding |Turkiye

Mechanical propertiesValues
Young’s modulus* 193 – 201 GPa
Specific stiffness* 24.7 – 25.7 MN.m/kg
Yield strength (elastic limit)324 – 415 MPa
Tensile strength662 – 795 MPa
Specific strength* 41.5 – 53.1 kN.m/kg
Elongation52 – 62 % strain
Compressive strength* 324 – 415 MPa
Flexural modulus* 193 – 201 GPa
Flexural strength (modulus of rupture)* 324 – 415 MPa
Shear modulus75 – 80 GPa
Poisson’s ratio* 0.265 – 0.275
Shape factor   55
Hardness – Vickers* 192 – 230 HV
Hardness – Rockwell B90 – 96 HRB
Hardness – Rockwell C* 9 – 18 HRC
Hardness – Brinell* 185 – 214 HB
Elastic stored energy (springs)* 309 – 511 kJ/m^3
Fatigue strength at 10^7 cycles278 – 308 MPa
Fatigue strength model (stress range)* 243 – 352 MPa
*Values indicated with asterisks (*) are approximate. No guarantee is provided for the precision of this information.
AISI 204-Cu Stainless steel, Annealed, Austenitic | 1.4597 |  Toughness | Fracture Toughness
AISI 204-Cu Stainless steel, Annealed, Austenitic | 1.4597 |  Carbon equivalency | Equivalent carbon content | CEV
AISI 204-Cu Stainless steel, Annealed, Austenitic | 1.4597 | Weldability  
AISI 204-Cu Stainless steel, Annealed, Austenitic | Chemical Composition  
AISI 204-Cu Stainless steel, Annealed, Austenitic | Designation | Equivalent Grades & Similar Grades  
Posted on

AISI 204-Cu Stainless steel, Annealed, Austenitic | Chemical Composition  

AISI 204-Cu Stainless steel-1.4597-X9CrMnCuNB17-8-3, S20430 Chemical Composition Modulus Metal Turkey Turkiye Manufacturing

Modulus Metal | Manufacturer Company in TURKEY: Sand Casting | Investment Casting | Foundry | CNC Machining | Press Bending | Laser Cutting | Welding | Plastics Injection Molding |Turkiye

Composition detail%
C (carbon) 0 – 0.15 %
Cr (chromium) 15.5 – 17.5 %
Cu (copper) 2 – 4 %
Fe (iron) * 64.5 – 74.4 %
Mn (manganese) 6.5 – 9 %
N (nitrogen) 0.05 – 0.25 %
Ni (nickel) 1.5 – 3.5 %
P (phosphorus) 0 – 0.06 %
S (sulfur) 0 – 0.03 %
Si (silicon) 0 – 1 %
*Values indicated with asterisks (*) are approximate. No guarantee is provided for the precision of this information.
AISI 204-Cu Stainless steel, Annealed, Austenitic | 1.4597 |  Toughness | Fracture Toughness
AISI 204-Cu Stainless steel, Annealed, Austenitic | 1.4597 |  Carbon equivalency | Equivalent carbon content | CEV
AISI 204-Cu Stainless steel, Annealed, Austenitic | 1.4597 | Weldability  
AISI 204-Cu Stainless steel, Annealed, Austenitic | Mechanical Properties
AISI 204-Cu Stainless steel, Annealed, Austenitic | Designation | Equivalent Grades & Similar Grades