| EN GJS 600 3 Cast iron, nodular graphite, Mechanical Properties |
|---|
| Young’s modulus 170 – 180 GPa |
| Flexural modulus * 170 – 180 GPa |
| Shear modulus 66 – 71 GPa |
| Bulk modulus 123 – 137 GPa |
| Poisson’s ratio 0.27 – 0.28 |
| Shape factor 22 |
| Yield strength (elastic limit) 370 – 415 MPa |
| Tensile strength 600 – 700 MPa |
| Compressive strength * 382 – 425 MPa |
| Flexural strength (modulus of rupture) 372 – 416 MPa |
| Elongation 3 – 7 % strain |
| Hardness – Vickers 220 – 255 HV |
| Fatigue strength at 10^7 cycles 248 – 280 MPa |
| Fatigue strength model (stress range) 165 – 212 MPa Parameters: Stress Ratio = 0, Number of Cycles = 1e7 |
| Fracture toughness * 22 – 54 MPa.m^0.5 |
| Mechanical loss coefficient (tan delta) * 0.001 – 0.0012 |
| *Values are approximations. This information’s accuracy is not guaranteed. |