| EN GJN HV600 (XCr11) Mechanical Properties, former BS 3F | Min | Max | |
|---|---|---|---|
| Young’s modulus | 165 | 220 | GPa |
| Specific stiffness | 21.1 | 28.3 | MN.m/kg |
| Yield strength (elastic limit) | *300 | 450 | MPa |
| Tensile strength | 300 | 450 | MPa |
| Specific strength | *38.4 | 57.8 | kN.m/kg |
| Elongation | *1 | 2 | % strain |
| Compressive strength | *500 | 900 | MPa |
| Flexural modulus | *165 | 220 | GPa |
| Flexural strength (modulus of rupture) | 720 | 920 | MPa |
| Shear modulus | 64 | 87 | GPa |
| Bulk modulus | 119 | 167 | GPa |
| Poisson’s ratio | 0.27 | 0.28 | |
| Shape factor | 23 | ||
| Hardness – Vickers | 450 | 700 | HV |
| Elastic stored energy (springs) | *240 | 523 | kJ/m^3 |
| Fatigue strength at 10^7 cycles | *120 | 180 | MPa |
| Fatigue strength model (stress range) Parameters: Stress Ratio = -1, Number of Cycles = 1e7cycles | *97.8 | 221 | MPa |
Values marked with * are approximate.
No guarantee is provided regarding the accuracy of this information.