Aluminum 6005 T1 Mechanical Properties

Designation

6005, wrought
Condition	T1 (Cooled from elevated temperature shaping process and naturally aged)
UNS number	A96005
EN name	EN AW-6005

Aluminum 6005 T1 Mechanical properties

Young’s modulus	67.5	–	71	GPa
Specific stiffness	24.9	–	26.3	MN.m/kg
Yield strength (elastic limit)	105	–	122	MPa
Tensile strength	170	–	198	MPa
Specific strength	38.8	–	45.1	kN.m/kg
Elongation	16	–	23	% strain
Compressive strength	105	–	122	MPa
Flexural modulus	67.5	–	71	GPa
Flexural strength (modulus of rupture)	105	–	122	MPa
Shear modulus	27	–	28.4	GPa
Bulk modulus	67.5	–	71	GPa
Poisson’s ratio	0.325	–	0.335
Shape factor	38.7
Hardness – Vickers	53	–	56	HV
Elastic stored energy (springs)	79.9	–	107	kJ/m^3
Fatigue strength at 10^7 cycles	97			MPa
Fatigue strength model (stress range) Parameters: Stress Ratio = -1, Number of Cycles = 1e7cycles	83.3	–	113	MPa