Ingot Iron Hot Rolled Mechanical Properties

Iron, commercial purity, ingot iron, hot rolled, >99.9%Fe

Ingot Iron Hot Rolled Mechanical Properties

Young’s modulus	204	–	212	GPa
Specific stiffness	25.9	–	26.9	MN.m/kg
Yield strength (elastic limit)	180	–	220	MPa
Tensile strength	275	–	345	MPa
Specific strength	22.9	–	28	kN.m/kg
Elongation	20	–	32	% strain
Compressive strength	180	–	220	MPa
Flexural modulus	204	–	212	GPa
Flexural strength (modulus of rupture)	180	–	220	MPa
Shear modulus	78	–	84	GPa
Bulk modulus	160	–	178	GPa
Poisson’s ratio	0.29	–	0.3
Shape factor	65
Hardness – Vickers	90	–	110	HV
Elastic stored energy (springs)	78.6	–	115	kJ/m^3
Fatigue strength at 10^7 cycles	110	–	175	MPa
Fatigue strength model (stress range)	102	–	189	MPa