EN GJN HV600 (XCr18) Mechanical Properties, former BS 3C | Min | Max | |
---|---|---|---|
Young’s modulus | 165 | 220 | GPa |
Specific stiffness | 21.1 | 28.3 | MN.m/kg |
Yield strength (elastic limit) | *300 | 450 | MPa |
Tensile strength | 300 | 450 | MPa |
Specific strength | *38.4 | 57.8 | kN.m/kg |
Elongation | *1 | 2 | % strain |
Compressive strength | *500 | 900 | MPa |
Flexural modulus | *165 | 220 | GPa |
Flexural strength (modulus of rupture) | 720 | 920 | MPa |
Shear modulus | 64 | 87 | GPa |
Bulk modulus | 119 | 167 | GPa |
Poisson’s ratio | 0.27 | 0.28 | |
Shape factor | 23 | ||
Hardness – Vickers | 510 | 700 | HV |
Elastic stored energy (springs) | *240 | 523 | kJ/m^3 |
Fatigue strength at 10^7 cycles | *120 | 180 | MPa |
Fatigue strength model (stress range) | *97.8 | 221 | MPa |
former BS 3C
Values marked with * are approximate.
No guarantee is provided regarding the accuracy of this information.