Aluminum A413.0 Die Cast (F) Material Data Sheet
Aluminum A413.0 Die Cast (F) Designation
| A413.0 (Aluminum Association) |
| Condition | F (As-fabricated) |
| UNS number | A14130 |
| EN number | EN AC-44100 / EN AC-Al Si12 |
Aluminum A413.0 Die Cast (F) Typical uses
| General purpose alloy: outdoor lamp housings, electronic cabinet frames, dental equipment |
Aluminum A413.0 Die Cast (F) Composition detail
| Al (aluminum) | 82.8 | – | 89 | % |
| Cu (copper) | 0 | – | 1 | % |
| Fe (iron) | 0 | – | 1.3 | % |
| Mg (magnesium) | 0 | – | 0.1 | % |
| Mn (manganese) | 0 | – | 0.35 | % |
| Ni (nickel) | 0 | – | 0.5 | % |
| Si (silicon) | 11 | – | 13 | % |
| Sn (tin) | 0 | – | 0.15 | % |
| Zn (zinc) | 0 | – | 0.5 | % |
| Other | 0 | – | 0.25 | % |
Aluminum A413.0 Die Cast (F) Physical properties
Aluminum A413.0 Die Cast (F) Mechanical properties
| Young’s modulus | 69.6 | – | 72.4 | GPa |
| Specific stiffness | 26.1 | – | 27.3 | MN.m/kg |
| Yield strength (elastic limit) | 105 | – | 116 | MPa |
| Tensile strength | 241 | – | 265 | MPa |
| Specific strength | 39.3 | – | 43.5 | kN.m/kg |
| Elongation | 3.5 | – | 4.2 | % strain |
| Compressive strength | 105 | – | 116 | MPa |
| Flexural modulus | 69.6 | – | 72.4 | GPa |
| Flexural strength (modulus of rupture) | 110 | – | 121 | MPa |
| Shear modulus | 26 | – | 27.4 | GPa |
| Bulk modulus | 65.2 | – | 74.5 | GPa |
| Poisson’s ratio | 0.322 | – | 0.338 | |
| Shape factor | 39 | | | |
| Hardness – Vickers | 86 | – | 96 | HV |
| Elastic stored energy (springs) | 77 | – | 93.9 | kJ/m3 |
| Fatigue strength at 10^7 cycles | 117 | – | 143 | MPa |
Fatigue strength model (stress range)
Parameters: Stress Ratio = -1, Number of Cycles = 1e7cycles | 113 | – | 148 | MPa |
Aluminum A413.0 Die Cast (F) Impact & fracture properties
| Fracture toughness | 24.1 | – | 28 | MPa.m0.5 |
| Toughness (G) | 8.22 | – | 11 | kJ/m2 |
Aluminum A413.0 Die Cast (F) Thermal properties
| Melting point | 572 | – | 584 | °C |
| Maximum service temperature | 150 | – | 170 | °C |
| Minimum service temperature | -273 | | | °C |
| Thermal conductivity | 149 | – | 161 | W/m.°C |
| Specific heat capacity | 944 | – | 982 | J/kg.°C |
| Thermal expansion coefficient | 20 | – | 21 | µstrain/°C |
| Thermal shock resistance | 71.2 | – | 80.1 | °C |
| Thermal distortion resistance | 7.2 | – | 7.91 | MW/m |
| Latent heat of fusion | 384 | – | 393 | kJ/kg |
Aluminum A413.0 Die Cast (F) Electrical properties
| Electrical resistivity | 4.3 | – | 4.5 | µohm.cm |
| Electrical conductivity | 38.3 | – | 40.1 | %IACS |
| Galvanic potential | -0.73 | – | -0.65 | V |
Aluminum A413.0 Die Cast (F) Magnetic properties
| Magnetic type | Non-magnetic |
Aluminum A413.0 Die Cast (F) Optical, aesthetic and acoustic properties
| Transparency | Opaque |
| Acoustic velocity | 5110 | – | 5230 | m/s |
| Mechanical loss coefficient (tan delta) | 0.0251 | – | 0.0296 | |
Aluminum A413.0 Die Cast (F) Processing properties
| Metal casting | Excellent |
| Metal cold forming | Unsuitable |
| Metal hot forming | Unsuitable |
| Metal press forming | Unsuitable |
| Metal deep drawing | Unsuitable |
| Machining speed | 39.6 m/min |
Weldability
Notes: Preheating is not required, post weld heat treatment is required | Excellent |
Aluminum A413.0 Die Cast (F) Durability
| Water (fresh) | Excellent |
| Water (salt) | Acceptable |
| Weak acids | Excellent |
| Strong acids | Excellent |
| Weak alkalis | Acceptable |
| Strong alkalis | Unacceptable |
| Organic solvents | Excellent |
| Oxidation at 500C | Unacceptable |
| UV radiation (sunlight) | Excellent |
Galling resistance (adhesive wear)
Notes: Aluminum alloys perform poorly when self-mated but can be processed without galling when mated with steels. | Limited use |
| Flammability | Non-flammable |
Aluminum A413.0 Die Cast (F) Corrosion resistance
Stress corrosion cracking
Note: Rated in chloride; Other susceptible environments: Halide, water | Slightly susceptible |
Aluminum A413.0 Die Cast (F) Notes
| Aluminum A413.0 Die Cast (F) Warning |
| Poor machinability, polishability and anodizing properties compared to other cast aluminum alloys |
Aluminum A413.0 Die Cast (F) Standards with similar compositions
| Australia: DA401 to AS 1874 |
| Belgium: AlSi12CuFe to NBN P21-101 |
| France: A-S12U to NF A50-702, A-S12U to NF A50-703 |
| International: AlSi12Cu to ISO 3522, AlSi12CuFe to ISO 3522 |
| Japan: AD1.1 to JIS H2118, AD1C.1 to JIS H2118, ADC1 to JIS H5302, ADC1C to JIS H5302 |
| Norway: 17512 to NS 17512 |
| Russia: AK12 to GOST 1583 |
| South Africa: SA42(Al-Si12FeA) to SABS 989 |
| Spain: L-2521 to UNE 38-269 |
| USA: A14130 to SAE J452, A413.0, A413.1, A413.1 to ASTM B179, S12A to ASTM B85, UNS A14130, UNS A14131 |
| Tradenames: AS 401, USCO 413.1 |
MODULUS METAL
Sand Casting in Turkey, Permanent Mold Casting in Turkey, Gravity Die Casting in Turkey, Pressure Die Casting in Turkey, High-Pressure Die Casting in Turkey, Investment Casting in Turkey, Foundry in Turkey, Plastic Injection Molding in Turkey, Press Bending ( Press Brake) Products in Turkey, Laser and Plasma Cutting in Turkey, Welded Construction in Turkey, Heat Treated, CNC Machined Products Manufacturer in Turkey, Additive Manufacturing and 3D Printing in Turkey, Quality Enginering and Inspection Service in Turkey, Manufacturing Inspection Service in Turkey, Quality Engineering and Supplier Quality Engineering Service in Turkey, Supplier Quality Control and Inspection Service in Turkey, Resident Engineering Services in Turkey