Home » Aluminum 413.0 Die Cast (F) Material Data Sheet
Aluminum 413.0 Die Cast (F) Material Data Sheet
Aluminum 413.0 Die Cast (F) Material Data Sheet
Aluminum 413.0 Die Cast (F) Designation
413.0 (Aluminum Association)
Condition
F (As-fabricated)
UNS number
A04130
EN number
EN AC-44100 / EN AC-Al Si12
Aluminum 413.0 Die Cast (F) Typical uses
General purpose alloy: architectural panels, outdoor lamp housings, food and dairy equipment
Aluminum 413.0 Die Cast (F) Composition detail
Al (aluminum)
82.2
–
89
%
Cu (copper)
0
–
1
%
Fe (iron)
0
–
2
%
Mg (magnesium)
0
–
0.1
%
Mn (manganese)
0
–
0.35
%
Ni (nickel)
0
–
0.5
%
Si (silicon)
11
–
13
%
Sn (tin)
0
–
0.15
%
Zn (zinc)
0
–
0.5
%
Other
0
–
0.25
%
Aluminum 413.0 Die Cast (F) Physical properties
Density
2.63
–
2.68
g/cm3
Aluminum 413.0 Die Cast (F) Mechanical properties
Young’s modulus
69.6
–
72.4
GPa
Specific stiffness
26.1
–
27.3
MN.m/kg
Yield strength (elastic limit)
138
–
152
MPa
Tensile strength
296
–
326
MPa
Specific strength
51.8
–
57.4
kN.m/kg
Elongation
2.5
–
3
% strain
Compressive strength
138
–
152
MPa
Flexural modulus
69.6
–
72.4
GPa
Flexural strength (modulus of rupture)
145
–
160
MPa
Shear modulus
26
–
27.4
GPa
Bulk modulus
65.2
–
74.5
GPa
Poisson’s ratio
0.322
–
0.338
Shape factor
36
Hardness – Vickers
89
–
100
HV
Elastic stored energy (springs)
134
–
163
kJ/m3
Fatigue strength at 10^7 cycles
100
–
117
MPa
Fatigue strength model (stress range) Parameters: Stress Ratio = -1, Number of Cycles = 1e7cycles
96
–
122
MPa
Aluminum 413.0 Die Cast (F) Impact & fracture properties
Fracture toughness
21.9
–
25.4
MPa.m0.5
Toughness (G)
6.78
–
9.05
kJ/m2
Aluminum 413.0 Die Cast (F) Thermal properties
Melting point
572
–
584
°C
Maximum service temperature
150
–
170
°C
Minimum service temperature
-273
°C
Thermal conductivity
116
–
126
W/m.°C
Specific heat capacity
944
–
982
J/kg.°C
Thermal expansion coefficient
20
–
21
µstrain/°C
Thermal shock resistance
93.9
–
106
°C
Thermal distortion resistance
5.63
–
6.18
MW/m
Latent heat of fusion
384
–
393
kJ/kg
Aluminum 413.0 Die Cast (F) Electrical properties
Electrical resistivity
4.3
–
4.5
µohm.cm
Electrical conductivity
38.3
–
40.1
%IACS
Galvanic potential
-0.73
–
-0.65
V
Aluminum 413.0 Die Cast (F) Magnetic properties
Magnetic type
Non-magnetic
Aluminum 413.0 Die Cast (F) Optical, aesthetic and acoustic properties
Transparency
Opaque
Acoustic velocity
5110
–
5230
m/s
Mechanical loss coefficient (tan delta)
0.036
–
0.0427
Aluminum 413.0 Die Cast (F) Processing properties
Metal casting
Excellent
Metal cold forming
Unsuitable
Metal hot forming
Unsuitable
Metal press forming
Unsuitable
Metal deep drawing
Unsuitable
Machining speed
30.5 m/min
Weldability Notes: Preheating is not required, post weld heat treatment is required
Excellent
Aluminum 413.0 Die Cast (F) Durability
Water (fresh)
Excellent
Water (salt)
Acceptable
Weak acids
Excellent
Strong acids
Excellent
Weak alkalis
Acceptable
Strong alkalis
Unacceptable
Organic solvents
Excellent
Oxidation at 500C
Unacceptable
UV radiation (sunlight)
Excellent
Galling resistance (adhesive wear) Notes: Aluminum alloys perform poorly when self-mated but can be processed without galling when mated with steels.
Limited use
Flammability
Non-flammable
Aluminum 413.0 Die Cast (F) Corrosion resistance
Stress corrosion cracking Note: Rated in chloride; Other susceptible environments: Halide, water
Slightly susceptible
Aluminum 413.0 Die Cast (F) Notes
Aluminum 413.0 Die Cast (F) Warning
Poor machinability, polishability and anodizing properties compared to other cast aluminum alloys
Aluminum 413.0 Die Cast (F) Standards with similar compositions
Hungary: OAlSi12Fe1 to MSZ 3713
Italy: 5079/GD-AlSi13Fe to UNI
Spain: L-2521 to UNE 38-203
USA: 413, 413 to QQ A-591E, 413.2, 413.2 to ASTM B179, 413.2 to QQ A-371F, A04130 to SAE J452, A413.0 to QQ A-591E, A413.1 to QQ A-371F, S12B to ASTM B85, UNS A04130, UNS A04132