| Designation | |
| 6061, wrought | |
| Condition | T651 (Solution heat-treated and artificially aged) |
| UNS number | A96061 |
| EN name | EN AW-6061 (EN AW-Al Mg1SiCu) |
| EN number | 3.3211 |
Aluminum 6061 T651 Mechanical Properties
| Young’s modulus | 66.6 | – | 70 | GPa |
| Specific stiffness | 24.5 | – | 25.8 | MN.m/kg |
| Yield strength (elastic limit) | 241 | – | 281 | MPa |
| Tensile strength | 274 | – | 320 | MPa |
| Specific strength | 88.8 | – | 104 | kN.m/kg |
| Elongation | 10 | – | 14.4 | % strain |
| Compressive modulus | 67.9 | – | 71.3 | GPa |
| Compressive strength | 241 | – | 281 | MPa |
| Flexural modulus | 66.6 | – | 70 | GPa |
| Flexural strength (modulus of rupture) | 241 | – | 281 | MPa |
| Shear modulus | 25.6 | – | 26.9 | GPa |
| Shear strength | 166 | – | 193 | MPa |
| Bulk modulus | 66.6 | – | 70 | GPa |
| Poisson’s ratio | 0.325 | – | 0.335 | |
| Shape factor | 24.7 | |||
| Hardness – Vickers | 100 | – | 107 | HV |
| Elastic stored energy (springs) | 427 | – | 576 | kJ/m^3 |
| Fatigue strength at 10^7 cycles | 106 | – | 124 | MPa |
| Fatigue strength model (stress range) Parameters: Stress Ratio = -1, Number of Cycles = 1e7cycles | 96.9 | – | 136 | MPa |
MODULUS METAL
Sand Casting in Turkey, Permanent Mold Casting in Turkey, Gravity Die Casting in Turkey, Pressure Die Casting in Turkey, High-Pressure Die Casting in Turkey, Investment Casting in Turkey, Foundry in Turkey, Plastic Injection Molding in Turkey, Press Bending ( Press Brake) Products in Turkey, Laser and Plasma Cutting in Turkey, Welded Construction in Turkey, Heat Treated, CNC Machined Products Manufacturer in Turkey